Diamond ASA C1030 6423 UVORE is a Acrylonitrile Styrene Acrylate material and is typically used in Extrusion, Injection Molding applications. Features include: Good Colorability, and Good Weather Resistance.
ASA C1030 6423 UVORE
Description
Availability
North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (220 °C/10.0 kg, Procedure A) | 10 g/10 min |
| Density - Specific Gravity | 1.1 g/cm³ |
| Tensile Strength at Yield (51 mm/min, Type I) | 45.9 MPa |
| Flexural Modulus (1.3 mm/min, 3.18 mm, Method I (3 point load), 50.8 mm, Tangent) | 1970 MPa |
| Tensile Elongation at Break (51 mm/min, Type I) | 30 % |
| Notched Izod Impact (23 °C, 3.18 mm) | 120 J/m |
| Deflection Temperature Under Load Unannealed (264 psi) (3.18 mm) | 67.8 °C |
| Deflection Temperature Under Load Unannealed (66 psi) (3.18 mm, Injection Molded) | 81.1 °C |
| Drying Time | 4.0 to 6.0 hr |
| Nozzle Temperature | 220 to 260 °C |
| Injection Rate | Fast |
| Drying Temperature | 80 to 85 °C |
| Front Temperature | 235 to 260 °C |
| Processing (Melt) Temp | 220 to 260 °C |
| Mold Temperature | 71 to 82 °C |
| Back Pressure | 0.517 to 1.03 MPa |
| Suggested Max Moisture | 0.02 % |
| Suggested Shot Size | 40 to 70 % |
| Middle Temperature | 232 to 260 °C |
| Rear Temperature | 230 to 260 °C |
Technical Data Sheet
Technical Data Sheet - APS InjectionProcess
Extrusion, Injection Molding
Resin
Acrylonitrile Styrene Acrylate