Polyaxis LP-8100 is a high density polyethylene intended for the rotational molding industry. This stiff yet tough compound was designed for watercraft products.
EXP LP 8100-31G BLACK V1
Description
Availability
North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (190 °C/2.16 kg) | 5.8 g/10 min |
| Density - Specific Gravity | 0.947 g/cm³ |
| Environmental Stress Crack Resistance (Compression Molded, F50, 10% Igepal) | 6.00 hr |
| Tensile Strength at Yield (51 mm/min, Rotational Molded) | 22.4 MPa |
| Flexural Modulus (Rotational Molded, 1% Secant) | 993 MPa |
| Tensile Elongation at Break (51 mm/min, Rotational Molded) | 200 % |
| Impact Strength (-40 °C, 3.18 mm, Rotational Molded) | 81 J |
| Impact Strength (-40 °C, 6.35 mm, Rotational Molded) | >258 J |
| Deflection Temperature Under Load Unannealed (264 psi) (3.18 mm, Rotational Molded) | 40.6 °C |
| Deflection Temperature Under Load Unannealed (66 psi) (3.18 mm, Rotational Molded) | 70.0 °C |
Technical Data Sheet
Technical Data Sheet - APSProcess
Rotomolding
Resin
Polyethylene, High Density, Metallocene