30 % glass fibre reinforced PP-Homopolymer, long term heat stabilized, low emission. Former product name: Polyfort FPP 30 GFC K1079
HOSTACOM FPP 30GFC K1079 BLK
Description
Availability
Africa-Middle East, Asia-Pacific, Europe, Latin America, North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Volume Flow Rate (230 °C/2.16 kg) | 5.0 cm³/10 min |
| Density (Method A) | 1.13 g/cm³ |
| Tensile Modulus (1 mm/min, Type 1A) | 6500 MPa |
| Tensile Stress at Break (Type 1A, 5 mm/min) | 85.0 MPa |
| Tensile Strain at Break (Type 1A, 5 mm/min) | 3.0 % |
| Flexural Modulus (2.0 mm/min) | 6000 MPa |
| Flexural Stress (2.0 mm/min, 3.6%) | 126 MPa |
| Flexural Stress (2.0 mm/min, 3.4%) | 128 MPa |
| Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A) | 10 kJ/m² |
| Charpy Impact Strength - Notched (-30 °C, Type 1, Edgewise, Notch A) | 8.0 kJ/m² |
| Charpy Impact Strength - Unnotched (23 °C, Type 1, Edgewise) | 48 kJ/m² |
| Charpy Impact Strength - Unnotched (-30 °C, Type 1, Edgewise) | 45 kJ/m² |
| Ball Indentation Hardness (H 358/30) | 128 MPa |
| Ball Pressure Test (145 °C) | Pass |
| Vicat Softening Temperature (B (50N), 50 °C/h) | 130 °C |
| Vicat Softening Temperature (A (10N), 50 °C/h) | 165 °C |
| Deflection Temperature Under Load Unannealed (0.45 MPa) (Flatwise) | 159 °C |
| Deflection Temperature Under Load Unannealed (1.80 MPa) (Flatwise) | 145 °C |
| Volume Resistivity | >1.0E+13 ohm*m |
| Surface Resistivity | >1.0E+15 ohm |
| Burning Rate (2.00 mm) | 58 mm/min |
| Burning Rate (2.00 mm) | 58 mm/min |
| Glow Wire Flammability Index (1.5 mm) | 750 °C |
| Glow Wire Flammability Index (3.0 mm) | 750 °C |
| Glow Wire Ignition Temperature (1.5 mm) | 775 °C |
| Glow Wire Ignition Temperature (3.0 mm) | 775 °C |
| Drying Time | 2.0 to 3.0 hr |
| Drying Temperature | 80 °C |
| Processing (Melt) Temp | 220 to 260 °C |
| Injection Rate | Moderate-Fast |
| Mold Temperature | 30 to 60 °C |
| Flammability Classification (1.5 mm) | HB |
| Flammability Classification (3.0 mm) | HB |
Technical Data Sheet
Technical Data Sheet - APS InjectionProcess
Injection Molding
Resin
Polypropylene, Homopolymer