Hifax ETA3104 BTFA PALE ADOBEmedium melt flow, 1,100 MPa flexural modulus, UV-stabilized thermoplastic elastomeric olefin (TEO) resin has a very good combination of properties and processability. It is typically used for a variety of molded-in color automotive exterior components.
Hifax ETA3104 BTFA PALE ADOBE
Description
Availability
North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (230 °C/2.16 kg) | 9 g/10 min |
| Density (23 °C) | 0.94 g/cm³ |
| Flexural Modulus | 1100 MPa |
| Tensile Stress at Yield | 20 MPa |
| Tensile Strain at Yield | 7 % |
| Notched Izod Impact Strength (23 °C) | 30 kJ/m² |
| Notched Izod Impact Strength (-40 °C) | 3.5 kJ/m² |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 85 °C |
| Deflection Temperature Under Load (1.80 MPa, Unannealed) | 55 °C |
| Mold Shrinkage |
Technical Data Sheet
Technical Data SheetProcess
Injection Molding
Resin
Polypropylene Compounds
Applications
Automotive Parts, Exterior Automotive Applications
Prohibited Applications of Compounded Polyolefins:
The following applications and/or end uses are prohibited by LyondellBasell. LyondellBasell will not solicit the sale of, or knowingly supply, product for use in the following applications:
FDA Class III medical devices, European Class III medical devices, Health Canada Class IV Medical Devices, applications involving permanent implantation into the body & life-sustaining medical applications