Hifax TRC 221P YZ9A BLK high melt flow, medium high flexural modulus, UV-stabilized, mineral-filled thermoplastic elastomeric olefin (TEO) resin combines processability with an excellent impact/stiffness balance. The grade is typically used for molding of large complex parts that require high impact strength as well as good stiffness.
Hifax TRC 221P YZ9A BLK
Description
Availability
North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (230 °C/2.16 kg) | 16 g/10 min |
| Density (23 °C, Method A) | 1.04 g/cm³ |
| Flexural Modulus (23 °C, 2 mm/min) | 1500 MPa |
| Tensile Stress at Yield (23 °C) | 17 MPa |
| Notched Izod Impact Strength (23 °C, Type 1, Notch A) | 47.0 kJ/m² |
| Notched Izod Impact Strength (-40 °C, Type 1, Notch A) | 3.4 kJ/m² |
| Heat Deflection Temperature A (1.80 MPa, Unannealed) | 48 °C |
| Mold Shrinkage |
Technical Data Sheet
Technical Data SheetProcess
Injection Molding
Resin
Polypropylene Compounds
Applications
Bumpers, Exterior Automotive Applications
Prohibited Applications of Compounded Polyolefins:
The following applications and/or end uses are prohibited by LyondellBasell. LyondellBasell will not solicit the sale of, or knowingly supply, product for use in the following applications:
FDA Class III medical devices, European Class III medical devices, Health Canada Class IV Medical Devices, applications involving permanent implantation into the body & life-sustaining medical applications