Moplen EP548S is a nucleated heterophasic copolymer with antistatic agent used injection moulding applications.
It combines a good impact/stiffness balance with a high fluidity.
Moplen EP548S is typically used by customers in opaque containers, housewares, toys and in thin-walled containers for food packaging (e.g. margarine tubs, yoghurt pots, etc.).
Moplen EP548S
Description
Availability
Africa-Middle East, Europe
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (230 °C/2.16 kg) | 44 g/10 min |
| Melt Flow Rate (230 °C/2.16 kg) | 44 g/10 min |
| Density | 0.90 g/cm³ |
| Density | 0.9 g/cm³ |
| Flexural Modulus | 1500 MPa |
| Tensile Modulus | 1550 MPa |
| Tensile Strength at Yield | 27 MPa |
| Tensile Stress at Yield | 28 MPa |
| Tensile Elongation at Yield | 4 % |
| Tensile Strain at Break | 30 % |
| Tensile Strain at Yield | 5 % |
| Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A) | 5 kJ/m² |
| Charpy Impact Strength - Notched (0 °C, Type 1, Edgewise, Notch A) | 3.5 kJ/m² |
| Charpy Impact Strength - Notched (-20 °C, Type 1, Edgewise, Notch A) | 3 kJ/m² |
| Notched Izod Impact Strength (23 °C) | 46 J/m |
| Ductile/Brittle Transition Temperature | -53 °C |
| Vicat Softening Temperature (A/50) | 151 °C |
| Deflection Temperature Under Load (0.46 N/mm²) | 116 °C |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 95 °C |
Process
Injection Molding
Resin
Polypropylene, Impact Copolymer
Applications
Housewares, Opaque Containers, Sports, Leisure & Toys