Perlex R3510 GREY 6-1811 is a Polycarbonate Glass Fiber, 10% filled material.
PERLEX R3510 GREY 6-1811
Description
Availability
Africa-Middle East, Asia-Pacific, Europe, Latin America, North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (300 °C/1.2 kg) | 10 g/10 min |
| Density | 1.25 g/cm³ |
| Tensile Stress at Yield | 75 MPa |
| Tensile Strain at Break | 5 % |
| Flexural Modulus | 3900 MPa |
| Tensile Strain at Yield | 5 % |
| Tensile Stress at Break | 83 MPa |
| Tensile Modulus | 4050 MPa |
| Flexural Stress | 135 MPa |
| Charpy Impact Strength - Notched (23 °C) | 6.0 kJ/m² |
| Charpy Impact Strength - Notched (-30 °C) | 6.0 kJ/m² |
| Charpy Impact Strength - Unnotched (-30 °C) | 58 kJ/m² |
| Charpy Impact Strength - Unnotched (23 °C) | 68 kJ/m² |
| Notched Izod Impact (Area) (23 °C) | 10.0 kJ/m² |
| Vicat Softening Temperature (B (50N), 50 °C/h) | 145 °C |
| Vicat Softening Temperature (A (10N), 50 °C/h) | 152 °C |
| Deflection Temperature Under Load Unannealed (0.45 MPa) | 135 °C |
| Deflection Temperature Under Load Unannealed (1.80 MPa) | 128 °C |
| RTI Elec (1.6 mm) | 80.0 °C |
| RTI Elec (3.2 mm) | 80.0 °C |
| RTI Imp (1.6 mm) | 80.0 °C |
| RTI Imp (3.2 mm) | 80.0 °C |
| RTI Str (1.6 mm) | 80.0 °C |
| RTI Str (3.2 mm) | 80.0 °C |
| Volume Resistivity | >1.0E+13 ohm*m |
| Comparative Tracking Index (CTI) | 175 V |
| Surface Resistivity | >1.0E+15 ohm |
| Burning Rate (2.00 mm) | 0.0 mm/min |
| Burning Rate (2.00 mm) | 0.0 mm/min |
| Glow Wire Ignition Temperature (3.0 mm) | 960 °C |
| Glow Wire Ignition Temperature (2.0 mm) | 960 °C |
| Glow Wire Ignition Temperature (1.0 mm) | 960 °C |
| Drying Time | 3.0 to 4.0 hr |
| Drying Temperature | 110 to 120 °C |
| Processing (Melt) Temp | 270 to 310 °C |
| Mold Temperature | 50 to 80 °C |
| Flame Rating (1.6 mm) | V-0 |
| Flame Rating (3.2 mm) | V-0 |
Technical Data Sheet
Technical Data Sheet - APS InjectionResin
Polycarbonate
Applications
Machine/Mechanical Parts