Petrothene LP510300 is a copolymer resin selected by customers for blown film applications. This resin offers high stiffness, excellent appearance, bubble stability, and good drawdown. LP510300 is recommended for merchandise bags, multi-wall sack liners, and barrier sheeting. It is also useful as a blend component for improved stiffness and machineability.
Availability
North America
Typical Properties
Melt Flow Rate (190 °C/2.16 kg)
0.33 g/10 min
Density (23 °C)
0.949 g/cm³
Dart Drop Impact Strength, F50
70 g
Tensile Strength at Break MD
43.4 MPa
Tensile Strength at Break MD
6300 psi
Tensile Strength at Break TD
31.0 MPa
Tensile Strength at Break TD
4500 psi
Tensile Strength at Yield MD
3600 psi
Tensile Strength at Yield MD
24.8 MPa
Tensile Strength at Yield TD
28.3 MPa
Tensile Strength at Yield TD
4100 psi
Tensile Elongation at Break MD
500 %
Tensile Elongation at Break TD
670 %
Secant Modulus MD
758 MPa
Secant Modulus MD
110000 psi
Secant Modulus TD
924 MPa
Secant Modulus TD
134000 psi
Elmendorf Tear Strength MD
31 g
Elmendorf Tear Strength TD
1200 g
Vicat Softening Temperature
126 °C
Vicat Softening Temperature
259 °F