Pro-fax SB786 impact polypropylene copolymer is available in pellet form. This resin is typically used in injection molding applications and offers good cold temperature impact and blush resistance.
ASTM and ISO-based versions of the technical data sheet are available for Pro-fax SB786.
Pro-fax SB786
Description
Availability
North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (230 °C/2.16 kg) | 8.0 g/10 min |
| Density (23 °C) | 0.90 g/cm³ |
| Density (23 °C, Method A) | 0.90 g/cm³ |
| Flexural Modulus (23 °C) | 1130 MPa |
| Flexural Modulus (0.05 in/min, 1% Secant, Procedure A) | 160000 psi |
| Flexural Modulus (1.3 mm/min, 1% Secant, Procedure A) | 1100 MPa |
| Tensile Strength at Yield (2 in/min) | 3700 psi |
| Tensile Strength at Yield (50 mm/min) | 26 MPa |
| Tensile Stress at Yield (23 °C) | 24 MPa |
| Tensile Elongation at Yield | 8 % |
| Tensile Strain at Yield (23 °C) | 9 % |
| Charpy Impact Strength - Notched (23 °C) | 8.2 kJ/m² |
| Charpy Impact Strength - Notched (-40 °C) | 1.9 kJ/m² |
| Notched Izod Impact Strength (23 °C) | 7.4 kJ/m² |
| Notched Izod Impact Strength (-40 °C) | 2.9 kJ/m² |
| Notched Izod Impact Strength (73 °F, Method A) | 1.6 ft-lb/in |
| Notched Izod Impact Strength (23 °C, Method A) | 85 J/m |
| Deflection Temperature Under Load (66 psi, Unannealed) | 175 °F |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 72 °C |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 79 °C |
| Deflection Temperature Under Load (1.80 MPa, Unannealed) | 48 °C |
Process
Injection Molding
Resin
Polypropylene, Impact Copolymer
Applications
Battery Cases