Pro-fax SV152 is a nucleated, very high impact polypropylene copolymer available in pellet form. This resin is typically used in general extrusion and blow molding applications and offers excellent cold temperature impact resistance.
ASTM and ISO-based versions of the technical data sheet are available for Pro-fax SV152.
Pro-fax SV152
Description
Availability
North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (230 °C/2.16 kg) | 1.4 g/10 min |
| Density (23 °C) | 0.90 g/cm³ |
| Density (23 °C, Method A) | 0.90 g/cm³ |
| Flexural Modulus (23 °C) | 1180 MPa |
| Flexural Modulus (0.05 in/min, 1% Secant, Procedure A) | 165000 psi |
| Flexural Modulus (1.3 mm/min, 1% Secant, Procedure A) | 1140 MPa |
| Tensile Strength at Yield (2 in/min) | 3500 psi |
| Tensile Strength at Yield (50 mm/min) | 24 MPa |
| Tensile Stress at Yield (23 °C) | 24 MPa |
| Tensile Elongation at Yield | 9 % |
| Tensile Strain at Yield (23 °C) | 8 % |
| Charpy Impact Strength - Notched (23 °C) | 85 kJ/m² |
| Charpy Impact Strength - Notched (-40 °C) | 4.2 kJ/m² |
| Notched Izod Impact Strength (23 °C) | 73 kJ/m² |
| Notched Izod Impact Strength (-40 °C) | 5.8 kJ/m² |
| Notched Izod Impact Strength (73 °F, Method A) | No Break ft-lb/in |
| Notched Izod Impact Strength (23 °C, Method A) | No Break J/m |
| Deflection Temperature Under Load (66 psi, Unannealed) | 195 °F |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 78 °C |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 95 °C |
| Deflection Temperature Under Load (1.80 MPa, Unannealed) | 49 °C |
Process
Extrusion Blow Molding, Sheet, Sheet and Profile Extrusion, Thermoforming
Resin
Polypropylene, Impact Copolymer
Applications
Automotive Parts, Corrugated Sheet, Opaque Containers