Pro-fax 6523 general purpose polypropylene homopolymer resin is available in pellet form.
ASTM and ISO-based versions of the technical datasheet are available for Pro-fax 6523.
Pro-fax 6523
Description
Availability
North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (230 °C/2.16 kg) | 4.0 g/10 min |
| Density (23 °C) | 0.90 g/cm³ |
| Density (23 °C, Method A) | 0.90 g/cm³ |
| Flexural Modulus | 1270 MPa |
| Flexural Modulus (0.05 in/min, 1% Secant, Procedure A) | 200000 psi |
| Flexural Modulus (1.3 mm/min, 1% Secant, Procedure A) | 1380 MPa |
| Tensile Strength at Yield (2 in/min) | 4800 psi |
| Tensile Strength at Yield (50 mm/min) | 33 MPa |
| Tensile Stress at Yield (23 °C) | 30 MPa |
| Tensile Elongation at Yield | 12 % |
| Tensile Strain at Yield (23 °C) | 12 % |
| Charpy Impact Strength - Notched (23 °C) | 6.7 kJ/m² |
| Notched Izod Impact Strength (23 °C) | 6.2 kJ/m² |
| Notched Izod Impact Strength (73 °F, Method A) | 1.0 ft-lb/in |
| Notched Izod Impact Strength (23 °C, Method A) | 53 J/m |
| Deflection Temperature Under Load (66 psi, Unannealed) | 190 °F |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 88 °C |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 79 °C |
| Deflection Temperature Under Load (1.80 MPa, Unannealed) | 50 °C |
Process
Cast Film, Injection Molding, Thermoforming
Resin
Polypropylene, Homopolymer
Applications
Automotive Parts, Raffia/Tapes/Strapping, Thermoformed Food Containers