Sequel E3400 UV NAT fractional melt flow, high flexural modulus thermoplastic polyolefin (TPO) is typically used for thermoformed exterior or interior applications that require low-temperature toughness and dimensional stability. This extrusion-grade material exhibits enhanced melt strength for a wide thermoforming processing window.
Sequel E3400 UV NAT
Description
Availability
North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (230 °C/2.16 kg) | 0.60 g/10 min |
| Density (23 °C) | 1.12 g/cm³ |
| Flexural Modulus (23 °C, 2 mm/min) | 2100 MPa |
| Tensile Stress at Yield (23 °C, 50 mm/min) | 21 MPa |
| Coefficent of Linear Thermal Expansion (CLTE) (-30 °C to 30 °C) | 4.9 x 10-5 cm/cm/°C |
| Coefficent of Linear Thermal Expansion (CLTE) (-30 °C to 30 °C) | 2.7 x 10-5 in/in/°C |
| Coefficent of Linear Thermal Expansion (CLTE) (-30 °C to 85 °C) | 5.8 x 10-5 cm/cm/°C |
| Coefficent of Linear Thermal Expansion (CLTE) (-30 °C to 85 °C) | 3.2 x 10-5 in/in/°C |
| Mold Shrinkage |
Technical Data Sheet
Technical Data SheetProcess
Thermoforming
Resin
Polypropylene Compounds
Applications
Industrial, Panels & Profiles
Prohibited Applications of Compounded Polyolefins:
The following applications and/or end uses are prohibited by LyondellBasell. LyondellBasell will not solicit the sale of, or knowingly supply, product for use in the following applications:
FDA Class III medical devices, European Class III medical devices, Health Canada Class IV Medical Devices, applications involving permanent implantation into the body & life-sustaining medical applications